High Purity White Castable Refractory Cement / High Alumina Cement CA-70 CA-75 CA-80
Quick Detail:
Model Number: CA-70 CA-75 CA-80
Al2O3 Content (%): 40%~80%
Material: Alumina Cement
Description:
Calcium aluminate cements are cements consisting predominantly of hydraulic calcium aluminates. Alternative names are "aluminous cement", "high-alumina cement" and "Ciment fondu" in French. They are used in a number of small-scale, specialized applications.
Applications:
1. In construction concretes, rapid strength development is achieved, even at low temperatures.
2. In construction concretes, high chemical resistance is possible.
3. In refractory concretes, strength is maintained at high temperatures.
4. As a component in blended cement formulations, various properties such as ultra-rapid strength development and controlled expansion can be obtained.
Specifications:
|
Product |
CA-65 |
CA-68 |
CA-70 |
CA-75 |
CA-80 |
|
|
Chemical Composition (%) |
Al2O3 |
64-66 |
67-69 |
69-71 |
73-75 |
77-80 |
|
CaO |
32-34 |
29-31 |
27-29 |
23-25 |
18-20 |
|
|
SiO2 |
1.8 |
1.2 |
0.3 |
0.3 |
0.3 |
|
|
Fe2O3 |
0.6 |
0.6 |
0.3 |
0.3 |
0.3 |
|
|
|
||||||
|
Specific Surface (cm2/g) |
4500 |
4500 |
5000 |
5500 |
7000 |
|
|
Setting time (h:min) |
Initial setting (min) |
0:40 |
0:40 |
0:40 |
0:45 |
0:45 |
|
Final Setting (min) |
8:00 |
8:00 |
10:00 |
10:00 |
10:00 |
|
|
|
||||||
|
Cold Modulus of Rupture (MPa) |
24 hour |
6.0min |
6.0min |
6.0min |
6.0min |
5.0min |
|
72 hour |
8.0min |
8.0min |
8.0min |
8.0min |
6.0min |
|
|
Cold Crushing Strength (Mpa) |
24hour |
45.0min |
45.0min |
45.0min |
45.0min |
35.0min |
|
72hour |
70.0min |
70.0min |
70.0min |
70.0min |
60.0min |
|
|
|
||||||
|
Refractoriness (°C) |
1680 |
1710 |
1730 |
1750 |
1770 |
|