95%-96% SiO2 Silica Refractory Bricks for Coke Oven, Glass Oven and Hot Air Furnace
Silica Brick Advantage:
1) Silicon oxide is above 95%.
2) Good acid erosion resistance.
3) High softening point with temperature.
4) No shrink in burn repeatedly.
5) Temperature of refractoriness under load is above 1650º C
Stable Capability, High Quality, Excellent Service, Competitive price is the most important advantage of our products.
This silica brick is used to the walls, hearth or other parts of the combustion chamber, and carbonization chamber
Application of silica brick:
They are widely used for hot blast furnace, coke oven, and glass furnace. The products can be made according to customers' requirement.
Silica Bricks specification:
Item | Coke Oven Silica Brick
| Glass Furnace Silica Brick | Hot Blast Stove Silica Brick
| |
| JJG-94
| JBG-95 | JBG-96 | JRG-95 | |
| SiO2 % | 94.5
| ≥95 | ≥96 | 95 |
| Fe2O3 % | 1.5
| ≤1.0 | ≤1.0 | 1.3 |
| CaO % | 2.5
| 2.2 | 2.2 | 2.2 |
| Refractoriness °C | 1790
| 1790 | 1790 | 1790 |
| Refractoriness under load T1,°C | 1650 | 1650 | 1660 | 1650 |
| Apparent porosity % | 22(24)
| 22(24) | 22(24) | 22(24) |
| Cold crushing strength Mpa | 40(35)
| 35(30) | 35(30) | 35(30) |
| True Density g/cm3 | 2.33
| 2.32 | 2.33 | 2.34 |
| Thermal Expansion % | 1000°C 1.28(1.30)
| 1000°C ≤1.25 | 1000°C ≤1.25 | 1000°C 1.26 |
| Residual Quartz % | 1.0
| 1.0 | 1.0 | 1.0 |