High Quality Cement Rotary Kiln Wear Resistant Red Silicon Mullite Brick For Cement Kiln
Silicon mullite brick by adopting high grade bauxite and SiC as raw material and special sintering process, silica mullite bricks are characterized by high strength, good performance of abrasion resistance and thermal shock resistance, constant forming protective layer for reducing accrection formation, long application cycle etc. silicon mullite fire brick is mainly designed for rotary kiln of cement industry, and silicon mullite firebrick is used for the transition zone, calcining zone of medium and small cement kiln.
Slilica mullite fire brick is mainly made of mullite as the main material and contain over 30percent SiO2 content and over 60 percent Al2O3 content. slilica mullite firebrick refractoriness generally is more than 1580 degree. silicate mullite fire brick is composed mainly of mullite, corundum, SiC and glass. refractory silicon mullite brick is formed at the junction of granules as mullite, glass and SiC. silicate mullite firebrick with high quality and various excellent properties for application in all kinds of high temperature furnace and kilns, such as roasting furnace.
.High temperature resistance,
.Erosion resistance,
.Wear resistance properties,
.Refiring small contraction,
.Excellent thermal shock resistance,
.Strong resistance to the corrosive gas and slag.
Silicon mullite block is made with raw material high grade bauxite and SiC and special sintering process. Silica mullite bricks are characterized by high density, good performance of abrasion resistance and thermal shock resistance. silicate mullite block can constantly form protective layer for reducing accrection formation, long application cycle.
1.Good acid and erosion resistance, powerful anti high-temperature strength.
2.Soften melting temperature is 1620~1670 °C.
3.Low thermal shock resistance.
4.Natural silica as raw material, plus regular mineralizer.
5.Ensure good bonding and structural strength of furnace.
6.Good heat resistance and long service life.
| Item | RS-AZM1650 | RS-AZM1680 |
| Sic + SiO2 | ≥ 30 | ≥ 32 |
| Al2O3 | ≥ 65 | ≥ 65 |
| Refractoriness Under Load | ≥ 1650 | ≥ 1680 |
| Apparent Porosity (%) | ≤ 19 | ≤ 19 |
| Thermal Shock Resistance | ≥ 15 | ≥ 20 |
| Bulk Density (g/cm3) | ≥ 2.65 | ≥ 2.70 |
| Cold Crushing Strength (Mpa) | ≥ 90 | ≥ 100 |