Zhengzhou Rongsheng Refractory Co., Ltd.
Zhengzhou Rongsheng Refractory Co., Ltd. Refractory manufacturing company.
Add to Cart
65%mgo magnesite chrome bricks refractory list of brick manufacturers
Product information
Magnesite chrome brick to magnesium oxide (MgO) and chromium oxide (Cr2O3) as the main ingredient,periclase and spinel as main mineral components of refractory products.
1. Common Magnesite chrome brick is made by sintered magnesia and refractory level chrome ore as raw materials. The space between refractory grains is bonded with silicate.
2. Direct-bonded Magnesite chrome brick is made by chrome ore with low content of impurities and pure magnesite,firing at the temperature above 1700°C.
3. Semi-rebonded and Fuse-rebonded magnesite chrome brick are made by fused magnesite chrome sinter.
Features
1. Low bulk density, low thermal conductivity, good thermal insulation performance.
2. Refractory category allow direct contact of fire, suitable ofr various atmosphere
3. Good integrity with furnace lining, long service life, easy operation, could be shaped freely
4. Product specification: standard form, normal standard, shaped and special shaped bricks.
5. Can be used in various kilns because of its cheapness and general tray package. Among all of the refractory materials, it is the most widely used.
Applications
1. Furnaces of metallurgy industry, heat treatment furnace
2. Furnaces of chemical industry and construction industry.
3. Furnace of incineration of garbage, recirculating fluidized bed furnace
Size
Standard sizing: 230 x 114 x 65 mm others up to the client
Special size and OEM Service also provide!
Physical and chemical indexes
Common magnesite chrome brick
| Item | MGe6 | MGe8 | MGe12 | MGe16 |
| MgO % | 80 | 72 | 70 | 65 |
| Cr2O3 % | 7 | 10 | 13 | 17 |
| CaO % | 1.2 | 1.2 | 1.2 | 1.2 |
| SiO2 % | 3.4 | 4 | 4 | 4.2 |
| Al2O3 % | 4.5 | 6.5 | 6 | 6 |
| Fe2O3 % | 4 | 4.8 | 5.5 | 6.5 |
| Apparent Porosity % | 17 | 18 | 18 | 18 |
| Bulk Density g/cm3 | 3 | 3 | 3.02 | 3.05 |
| Cold Crushing Strength Mpa | 55 | 55 | 55 | 50 |
| Refractoriness Under Load °C | 1600 | 1600 | 1600 | 1600 |
Direct-Bonded magnesite chrome brick
| Item | DMGe4 | DMGe8 | DMGe12 | DMGe16 |
| MgO % | 85 | 77 | 74 | 69 |
| Cr2O3 % | 5.5 | 9.1 | 14 | 18 |
| CaO % | 1.1 | 1.4 | 1.2 | 1.2 |
| SiO2 % | 1.3 | 1.2 | 1.2 | 1.5 |
| Al2O3 % | 3.5 | 4 | 3.5 | 4.5 |
| Fe2O3 % | 3 | 6.4 | 5 | 5.7 |
| Apparent Porosity % | 18 | 18 | 18 | 18 |
| Bulk Density g/cm3 | 3.02 | 3.04 | 3.06 | 3.08 |
| Cold Crushing Strength Mpa | 50 | 50 | 55 | 55 |
| Refractoriness Under Load °C | 1700 | 1700 | 1700 | 1700 |
| Thermal expansion %(at 1000°C) | 1 | 1 | 1 | 0.9 |
| Thermal expansion %(at 1600°C) | 1.8 | 1.8 | 1.8 | 1.6 |