Name: Basic Open Hearth Furnace Magnesite Brick 95 Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee
Brand: RONGSHENG
Price: 1 USD

Ask Latest Price

Video Channel

Brand Name :RONGSHENG

Certification :ISO9001

Place of Origin :Henan, China

MOQ :1 Ton

Chemical Composition :Al2O3-SiO2

Thermal Conductivity (W/M·K) :1.3-1.5

Carbon Content :99%

Raw Materials :Phosphate

Cold Crushing Strength (Mpa) :20-40

Refractoriness Under Load :Min 1620°C

Fe2O3 Content (%) :1.5-2.5

Standard Size :Customized size

Apparent Porosity (%) :18-26

Oem Odm :Acceptable

Density :2.3g/cm3

Transportation :Shipping

Working Temperature :1450℃

Use :lime kiln and other kiln project

Bulk Density :0.9g/cm3

Contact Now

Add to Cart

View Product Description

Product Description

Magnesite Brick Introduction Magnesia Bricks are alkaline refractory materials. These products have over 90% magnesium oxide content and adopt periclase as the principal crystalline phase. Magnesia Bricks can be divided into two categories of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. They have excellent performance of superior high temperature mechanical strength and volume stability. Magnesia Bricks can service in the high temperature of 1750℃. They are ideal products for glass furnace application. 

Magnesia Bricks generally can be classified into two types of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. 1. Burnt Magnesia Bricks have high purity and firing temperature as the direct contact with periclase crystalline grain. 2. Chemical bonded magnesite brick is made of fused magnesite as the raw material. Magnesium Refractory Bricks Specifications Rongsheng MGO contents range from 85% to 98% Widely used throughout metallurgical industry

Features

Magnesium Refractory Bricks Features1.High refractoriness, usually the refractoriness is above 2000°C. 2.Strong ability to resist basic (alkaline) slag, can not contact with acid refractory material. 3.Strong ability of thermal conductivity, sometime need insulating material. 4.Excellent resistance in slag abrasion,Higher bulk density 5.Lower apparent porosity and Lower impurity content

Specification

Rongsheng Refractory Magnesia Brick Technical Data:

Brand	MZ-92	MZ-95	MZ-97	MZ-98
MgO % ≥	92	95	97	98
CaO % ≤	2	1.7	1.3	1.2
SiO2 % ≤	1.2	1	0.7	0.6
Fe2O3 % ≤	1.2	1	0.8	0.5
Bulk Density≥ g/cm3	2.9	2.95	2.95	3
A.P. % ≤	16	16	16	15
C.C.S (Mpa) ≥	60	70	70	80
0.2mpa Refractoriness under load T0.6 ≥ °C	1530	1650	1700	1700

Shapes &Sizes of Rongsheng Magnesite Refractory Brick:

Straight	Split	Arch	Wedge	Tile	Other Shape
L×W×H(mm)	L×W×H (mm)	L×W×H/h(mm)	L×W×H/h (mm)	L×W×H (mm)	Key brick,
230×114×65	230×114×25	230×114×65/45	230×114×65/45	230×230×38	Skew brick,
230×114×75	230×114×32	230×114×65/55	230×114×65/55	230×230×50	Soap,
	230×114×37	230×114×75/45	220×114×75/45	230×230×65	Checker,
	230×114×50	230×114×75/55	220×114×75/55	230×230×75	Neck,
		230×114×75/65	220×114×75/65		Taper,
We also can make brick according to customers' drawing and requirements.

Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee

Kiln Refractory Bricks

Refractory Fire Bricks

High Alumina Refractory Brick

Micro Nano Insulation Material

Zirconium Silicate Ceramics

Fireclay Brick

Refractory Raw Materials

Silica Refractory Bricks

Magnesia Bricks

Corundum Brick

Insulating Fire Brick

Mullite Brick

Refractory Castable

Refractory Products

Ceramic Fiber Blanket

Furnace Bricks

Fireplace Refractory Brick

Graphite Electrode

Basic Open Hearth Furnace Magnesite Brick 95% Mgo Fused And Sintered Magnesia Brick Magnesium Refractory Bricks For Stee

magnesite refractory bricks

magnesite refractory brick

mgo refractory bricks