Name: Wholesale 92 98 Mgo Magnesia Refractories High Performance Magnesite Refractory Bricks For Industrial Kilns
Brand: RONGSHENG
Price: 1 USD

Ask Latest Price

Video Channel

Brand Name :RONGSHENG

Certification :ISO9001

Place of Origin :Henan, China

MOQ :1 Ton

Cold Crushing Strength :≥40MPa

Origin :Xinmi

Calcium Oxide Content :≤15%

Type :Porosity Type Insulating Brick

Aluminum Content :≥35%

Porosity :≤22%

Material :Fireclay

Application :Kiln lining, furnace lining

Ash :0.3%

Size :230x114x65mm

Keyword :low porosity fire clay brick

Color :Light yellow

Way Of Construction :Daubing or casting

Maximum Service Temp :1500

Diameter :200mm-800mm

Contact Now

Add to Cart

View Product Description

Product descriptions from the supplier

Product Description

Magnesia Bricks Introduction Magnesia Bricks, a kind of basic refractory with more than 90% magnesium oxide content, are made of periclase as the main crystal phase. Magnesia Brick is mainly used in basic open-hearth furnace for steelmaking, electric furnace, rotary cement kiln, heating furnace, glass furnace and hyperthermia tunnel kiln with properties of higher refractoriness, good basic slag erosion resistance and high apparent initial softening temperature. Magnesia Bricks Classification Magnesia Bricks generally can be classified into two types of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. 1. Burnt Magnesia Bricks have high purity and firing temperature as the direct contact with periclase crystalline grain. 2. Chemical bonded magnesite brick is made of fused magnesite as the raw material.

Features

Magnesia Bricks Features 1.High refractoriness, usually the refractoriness is above 2000°C. 2.Strong ability to resist basic (alkaline) slag, can not contact with acid refractory material. 3.Strong ability of thermal conductivity, sometime need insulating material. 4.Excellent resistance in slag abrasion,Higher bulk density 5.Lower apparent porosity and Lower impurity content

Specification

Rongsheng Refractory Magnesia Brick Technical Data:

Brand	MZ-92	MZ-95	MZ-97	MZ-98
MgO % ≥	92	95	97	98
CaO % ≤	2	1.7	1.3	1.2
SiO2 % ≤	1.2	1	0.7	0.6
Fe2O3 % ≤	1.2	1	0.8	0.5
Bulk Density≥ g/cm3	2.9	2.95	2.95	3
A.P. % ≤	16	16	16	15
C.C.S (Mpa) ≥	60	70	70	80
0.2mpa Refractoriness under load T0.6 ≥ °C	1530	1650	1700	1700

Shapes &Sizes of Rongsheng Magnesium Oxide Brick:

Straight	Split	Arch	Wedge	Tile	Other Shape
L×W×H(mm)	L×W×H (mm)	L×W×H/h(mm)	L×W×H/h (mm)	L×W×H (mm)	Key brick,
230×114×65	230×114×25	230×114×65/45	230×114×65/45	230×230×38	Skew brick,
230×114×75	230×114×32	230×114×65/55	230×114×65/55	230×230×50	Soap,
	230×114×37	230×114×75/45	220×114×75/45	230×230×65	Checker,
	230×114×50	230×114×75/55	220×114×75/55	230×230×75	Neck,
		230×114×75/65	220×114×75/65		Taper,
We also can make brick according to customers' drawing and requirements.