Name: High Temperature Refractory Clay Brick Price Fire Resistant Firelay Bricks Cheap Fire Brick For Furnaces
Brand: RONGSHENG
Price: 1 USD

Ask Latest Price

Video Channel

Brand Name :RONGSHENG

Certification :ISO9001

Place of Origin :Henan, China

MOQ :1 Ton

Diameter :200mm-800mm

Ash :0.3%

Weight Of Brick :3-4KG/Pices

Chemical Composition :Al2O3: 38-42%, SiO2: 50-55%, Fe2O3: 1-2%

Installation Method :Vibration

Transportation :Shipping

Keyword :low porosity fire clay brick

Calcium Oxide Content :≤15%

Refractorines :36

Work Temperature :1400C

Crushing Strength :40~60 Mpa

Cold Compressive St :Min 100

Iron Content :≤2.0%

Cold Crushing Strength (Mpa) :20-60

Material :Fireclay

Contact Now

Add to Cart

View Product Description

Product descriptions from the supplier

Product Description

Fire Clay Bricks Description:Fireclay bricks refer to clay products with Al2O3 content of 30%~48%. The fire resistance can reach 1690~1730 ℃. Refractory clay brick is made of clinker clay through mixing, molding, drying, sintering and proportioning. It has good corrosion resistance, wear resistance, thermal shock resistance, spelling resistance, high mechanical strength, and good volume stability under high temperature. We bring forth high quality fire clay Bricks, which is manufactured to meet the requirements of neutral refractoriness where safe working temperature is more than 1450 degree centigrade. We offer fire clay Bricks in different specifications as per customer requirements. Refractory Fire Clay Brick: Standard sizing: 230 x 114 x 65 mm ,Special size and OEM Service also provide! The size is precise, providing kinds of shapes according to customer's drawing

Features

Fire Clay Bricks Features:

Good resistance to corrosion and abrasion;2.Perfect thermal shock resistance;
Good spalling resistance;
High mechanical strength;
Good volume stability under high temperature;
Excellent thermal performance, and acid resistance;

Product Parameters

Rongsheng Refractory Fire Clay Brick Technical Data:

Item	Fire Clay Brick SK-32	Fire Clay Brick SK-34	Fire Clay Brick SK-36
AI2O3(%)	30	38	50
Fe2O3 (%)	3	2.5	2
Refractoriness (SK)	32	34	36
Refractoriness under load, 0.2MPa, Ta, ((°C)	1300	1350	1450
Porosity (%)	22-26	19-23	20-24
Bulk density (g/cm³)	2.05	2.10-2.15	2.30-2.40
Cold crushing strength (MPa)	25	25	45
Thermal expansion at 1000°C (%)	0.6	0.6	0.3